Copper clad aluminum/steel production line

0

Copper by area

15%CCA

12%CCA

10%CCA

Copper by weight

38%

32%

30%

Machine type

VTL-10

VTL-12

VTL-14

1 

Raw material

Aluminum rod

mm

raw

Φ9.5

Φ12

Φ15

Pre-drawing

→9.0/8.6

→11.5/11.0/10.6

14.3/13.613.0/12.6

degrease

Φ8.6

Φ10.6

Φ12.6

Copper stripmm

31.4*0.38~0.40

37.7*0.36~0.38

44.0*0.38~0.40

2

 

Brush and wrapping

and weldingmm

Φ10

Φ12

Φ14

3

Drawing by slowly for no bonded

4

Metallurgically bonded

CCA

Φ3.0

Φ4.2

Φ5.6

CCAM

Φ2.5

//

//

5

Fast drawing after bonded

6

Degrease and testing and winding

7

Fine drawing

Well type annealing for final big size wire

8

Continue pipe type annealing for final fine wire

9

Capacity per day

 (22 hours )

1.8tons

2.5tons

3.2 tons

10

Min. wire size after drawing

0.12mm

0.18mm

1.0mm

The machine is use clad –welding technique, the wire is made by fusing core aluminum with external copper cladding. These two difference kinds of metals are metallurgical bonded at their interface and the copper –cladding thickness remains constant, so they become a single and in dissociable wire.

About us|News|Products|Services|After-sale service|Feedback|Download|Contact us
Add:18-A,JingHong DaLou,NO.508, Yishan Road,Shanghai,200235
Tel: 86-21-64879030,64879031      Fax: 86-21-54259031
E-mail: info@sinoleader.com, sinoleader@163.com      MSN:       Skype Name: sinoleader